Bosim | Doimiy haroratda sinov bosimi (MPa) | Amaldagi harorat | Amaldagi vosita
| |||
Qobiq testing | Yuqori bosimli muhr | Past bosimli muhr | ||||
Nominal reyting preishonch (PN) | 1.6 | 2.4 | 1.76 | 0,6 | -29~121℃ | Tabiiy gaz, suyultirilgan gaz, ko'mir gazi, neft, suv, talab |
2.5 | 3.75 | 2.75 | 0,6 | |||
4.0 | 6.0 | 4.4 | 0,6 | |||
6.4 | 9.6 | 7.04 | 0,6 | |||
10.0 | 15.0 | 11.0 | 0,6 | |||
16.0 | 24.0 | 17.6 | 0,6 | |||
Bosim sinflari (sinf) | 150 | 2.94 | 2.16 | 0,6 | ||
300 | 7.67 | 5.62 | 0,6 | |||
400 | 10.2 | 7.48 | 0,6 | |||
600 | 15.3 | 11.23 | 0,6 | |||
900 | 23.0 | 16.85 | 0,6 | |||
1500 | 39,0 | 28.6 | 0,6 |
Texnik spetsifikatsiya
Design havolasi | GB | API | MENDEK | |
Dizayn standarti | GB/T12237 | API6D | ASME B16.34 | |
Strukturaviy uzunlik | Flanesli uchlari | GB/T12221 | API6D | ASME B16.10 |
Payvandlangan ulanish | GB/T12221 | |||
Flanesli uchis | GB/T9113JB/T79 | ASME B16.5 | ||
Bizlding tugaydi | GB/T12224 | ASME B16.25 | ||
Sinov va tekshirish | GB/T13927 JB/T9092 | API6D | API598 |
Eslatma: Vana birlashtiruvchi gardish va payvand choklarining o'lchamlari mijozning talabiga binoan ishlab chiqilishi mumkin.
Asosiy qismlar Materiallar shakli
Yo'q. | Accessory name | Material | |
GB | ASTM | ||
1 | Tana | ZG25Mn | A352-LCB |
2 | O'rindiq | PTFE | PTFE |
3 | To'p | 25Mn+ENP | A350-LFI+ENP |
4 | Shlangi | Grafit+06Cr18Ni9Ti | Grafit+304 |
5 | Stud | 35CrMoA | A320-L7 |
6 | Yong'oq | 45 | A194-4 |
7 | Kaput | ZG25Mn | A352-LCB |
8 | Poyasi | 12Cr13 | A182-F6a |
9 | Shlangi | PTFE | PTFE |
10 | Shlangi | PTFE | PTFE |
11 | Shlangi | Grafit | Grafit |
12 | Yong'oq | 45 | A194-2H |
13 | Stud | 35CrMoA | A193-B7 |
14 | Bo'yinturuq | ZG25Mn | A352-LCB |
15 | Qadoqlash | Grafit+1Cr18N19Ti | Grafit+304 |
16 | Qadoqlash bezi | ZG25Mn | A352-LCB |
17 | Joylashuv qismi | Q235A | A36 |
18 | Ring | 65 mln | AISI1566 |
19 | Kalit | WCB | A216-WCB |
20 | Vida mix | 35CrMoA | A193-B7 |